Diseño de hormigón de altas prestaciones con agregados de cuarcita para su aplicación en el ámbito vial, estructural y arquitectónico con adición de pigmentos
dc.contributor.advisor | Almache Sánchez, Luis Mario | |
dc.contributor.author | Vallejo Barahona, Edgar Alejandro | |
dc.contributor.cedula | 1400755243 | es_ES |
dc.coverage | Cuenca – Ecuador | es_ES |
dc.date.accessioned | 2020-08-13T17:31:25Z | |
dc.date.available | 2020-08-13T17:31:25Z | |
dc.date.issued | 2016 | |
dc.description | La investigación llevada a cabo en el presente documento, tiene como finalidad, encontrar el comportamiento óptimo de los hormigones de altas prestaciones con agregados de cuarcita, mediante la adición de pigmentos, las mismas que están siendo utilizadas, y cada vez más, en la actualidad en diferentes tipos de hormigones. Con este objetivo, se utilizó la norma ACI 211-4R-98, que describe el procedimiento para el diseño de mezclas de hormigones de altas prestaciones. Se emprende nuestra investigación con la determinación de las propiedades físicas y mecánicas de los agregados de cuarcita y del cemento Guapán, se obtuvo mezclas patrón con las respectivas probetas, las mismas que fueron ensayadas a las edades de 3, 7 y 28 días. Del análisis de estos resultados, se elaboró la mezcla prueba, añadiendo el hiperplastificante con ensayos a los 3,7 y 28 días. De los valores obtenidos finalmente, se concluyó con las mezclas definitivas, añadiendo pigmentos en diferentes proporciones, que de acuerdo a las normas internacionales se debe aplicar entre un 3% a un 6% de pigmento por cantidad de cemento según el peso, y se consiguió su relación más eficiente económicamente. Para la elaboración de los hormigones de las mezclas mencionadas, se utilizarán áridos procedentes del sector El Panecillo, perteneciente al cantón Logroño, y cemento portland Puzolánico tipo IP Guapán, hormigones que deberán tener una resistencia requerida de 598 kg/cm2, partiendo de una resistencia de diseño a la compresión de 500 kg/cm2. En general, para hormigones de altas prestaciones, su relación de a/c es muy baja, por lo que, reflejan mezclas de consistencia muy secas y baja trabajabilidad, por ende es indispensable el uso de aditivos híperplastificantes, que brinden a la mezcla mayor trabajabilidad y nos ayude a un fácil proceso de compactación en obra. | es_ES |
dc.description.resumen | The research carried out in this paper, is aimed to find the optimal behavior of high performance concrete with aggregates of quartzite, by adding pigments, thereof being used, and increasingly, currently in different types of concrete. With this aim, the standard ACI 211-4R-98 was used, describing the procedure for designing mixtures of high-performance concretes. Our research is undertaken on determining the physical and mechanical properties of quartzite aggregates and the Guapán cement, mixtures pattern was obtained with the corresponding samples, the same ones that were tested at the ages of 3, 7 and 28 days. From the analysis of these results, the test mixture was prepared by adding the hyper-plasticizer at 3, 7 and 28 days. The values obtained finally, we concluded with the final mixes, adding pigments in varying proportions, which according to international standards between 3% and 6% of pigment of cement quantity by weight must be applied, and a more efficient relationship economically was possible. For the preparation of concrete mixtures as the above, aggregates from the area of El Panecillo were used, belonging to the Logroño canton, portland pozzolan cement type Guapán IP, concretes must have a required strength of 598 kg / cm2, starting from a design resistance compression 500 kg / cm2. In general, high-performance concrete, its ratio a / c is very low, therefore, they reflect very dry consistency and workability mixtures, therefore it is essential the use of hyper-plasticizers additives, which provides greater mix workability and help us easily in the compacting process. | es_ES |
dc.format | application/pdf | es_ES |
dc.format.extent | xiii, 153 páginas | es_ES |
dc.identifier.other | 5BT2016-TC53 | |
dc.identifier.uri | https://dspace.ucacue.edu.ec/handle/ucacue/1817 | |
dc.language.iso | spa | es_ES |
dc.publisher | Universidad Católica de Cuenca. Carrera de Ingeniería Civil | es_ES |
dc.rights | Atribución 4.0 Internacional | |
dc.rights | info:eu-repo/semantics/openAccess | es_ES |
dc.rights.uri | http://creativecommons.org/licenses/by/4.0/deed.es | |
dc.source | Universidad Católica de Cuenca | es_ES |
dc.source | Repositorio Institucional - UCACUE | es_ES |
dc.subject | Diseño De Hormigones | es_ES |
dc.subject | Hormigón De Altas Prestaciones | es_ES |
dc.subject | Agregados De Cuarcita | es_ES |
dc.subject | Hormigón Pigmentado | es_ES |
dc.title | Diseño de hormigón de altas prestaciones con agregados de cuarcita para su aplicación en el ámbito vial, estructural y arquitectónico con adición de pigmentos | es_ES |
dc.type | info:eu-repo/semantics/bachelorThesis | es_ES |
dc.type | info:eu-repo/semantics/publishedVersion | es_ES |
thesis.degree.discipline | Carrera de Ingeniería Civil | es_ES |
thesis.degree.level | Título Profesional | es_ES |
Archivos
Bloque original
1 - 1 de 1
Cargando...
- Nombre:
- VALLEJO B. EDGAR A..pdf
- Tamaño:
- 15.65 MB
- Formato:
- Adobe Portable Document Format
- Descripción: