Diseño de mezcla para hormigón simple de 240 kg/cm2 utilizando fibras de materiales reciclados

dc.contributor.advisorSolá Quintuña, Juan Medardo
dc.contributor.authorMendieta Yunga, Edwin Ronald
dc.contributor.cedula106025059es_ES
dc.coverageCuenca – Ecuadores_ES
dc.date.accessioned2020-08-13T17:31:31Z
dc.date.available2020-08-13T17:31:31Z
dc.date.issued2016
dc.descriptionEsta investigación propone el diseño de un nuevo tipo de hormigón simple f´c = 240 Kg/cm2, a partir de plásticos reciclados; y según los resultados obtenidos en el proceso de estudio se ha mejorado la resistencia a compresión y la resistencia a la flexión. Para la propuesta, se diseñó una maquina artesanal, para el corte de botellas recicladas, la misma que funciona a base de energía eléctrica y permite obtener fibra de diferentes tamaños para el hormigón; a más de ello permite la reutilización de materiales reciclables y el fomento de buenas prácticas ambientales. A partir del diseño de las mezclas de hormigón, se utilizó una prensa para roturas de las muestras, con la cual se ha registrado todos los datos de resistencia a compresión y a flexión; también se construyó encofrados de madera, para losas de 0,07m x 0,5m x 1,14m; con diferentes porcentajes de fibras a las que se aplicará carga y se determinará su comportamiento. Para las comparaciones de los resultados se realizaron pruebas con hormigones simples normales y experimentales, con 3 tipos de tamaños de fibras y 3 tipos de porcentajes diferentes. Los resultados registrados fueron positivos y a la vez se apreciaron comportamientos que en un hormigón simple normal no las hay. Se realizaron algunas pruebas para mejorar la resistencia a compresión y de igual manera las resistencias a la flexión, en donde los resultados estuvieron por encima del hormigón simple normal. En el desarrollo del estudio se ha generado un glosario de términos técnicos, tablas, gráficas, ilustraciones, visitas de campo, a fin de obtener una investigación elemental y probada para la colectividad. Después de haber concluido con las pruebas y los análisis de la investigación se puede decir que se ha cumplido con lo que se esperaba obtener; un hormigón con resistencias superiores a hormigones normales y a la vez ayuda ambientalmente en la reutilización de botellas de plástico mediante su recolección.es_ES
dc.description.resumenThis research proposes the design of a new type of single concrete fc = 240 Kg /cm2, based on recycled plastics; and according to the results obtained in the studyprocess the compressive and flexural strength has been improved. For the proposal, a craft machine was designed for cutting recycled bottles, which runs on electricity and allows to obtain different fiber sizes for concrete; also the reuse of recyclable materials and promote good environmental practices. Based on the design of concrete mixes, a press for cracks was used for the samples, with which all compressive strength and flexural data was recorded; wood forms are also built for slabs 0.07M x 0,5m x 1,14m; with different percentages of fibers to which load will be applied and determine its behavior. Comparing the results using standard tests, experimental and simple concrete was performed, with three types of fiber sizes and 3 different types of percentages. The results were positive and the behaviors registered in a normal plain concrete were observed. Some tests to improve the compressive strength and likewise the flexural strengths, where the results were above the normal single concrete. During the develop of the study a glossary of technical terms, tables, graphs, illustrations, field visits has been generated, in order to obtain a basic research and tested for the community. After having completed the testing and analysis of the research we can say that it has been done what was expected to obtain; concrete with above resistance over normal concrete and at the same time environmentally aid in the reuse of collected.es_ES
dc.formatapplication/pdfes_ES
dc.format.extentxiv, 61 páginases_ES
dc.identifier.other5BT2016-TC49
dc.identifier.urihttps://dspace.ucacue.edu.ec/handle/ucacue/1830
dc.language.isospaes_ES
dc.publisherUniversidad Católica de Cuenca. Carrera de Ingeniería Civiles_ES
dc.rightsAtribución 4.0 Internacional
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/deed.es
dc.sourceUniversidad Católica de Cuencaes_ES
dc.sourceRepositorio Institucional - UCACUEes_ES
dc.subjectDiseño De Hormigónes_ES
dc.subjectReciclaje De Botellases_ES
dc.subjectFibras De Plásticoes_ES
dc.subjectHormigón Simplees_ES
dc.titleDiseño de mezcla para hormigón simple de 240 kg/cm2 utilizando fibras de materiales recicladoses_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
dc.typeinfo:eu-repo/semantics/publishedVersiones_ES
thesis.degree.disciplineCarrera de Ingeniería Civiles_ES
thesis.degree.levelTítulo Profesionales_ES
Archivos
Bloque original
Mostrando 1 - 1 de 1
Cargando...
Miniatura
Nombre:
MENDIETA Y. EDWIN R..pdf
Tamaño:
5.88 MB
Formato:
Adobe Portable Document Format
Descripción: