Por favor, use este identificador para citar o enlazar este ítem: https://dspace.ucacue.edu.ec/handle/ucacue/13161
Registro completo de metadatos
Campo DC Valor Lengua/Idioma
dc.contributor.advisorGonzález Rodríguez, Geovanny-
dc.contributor.authorUrgiles Sarmiento, Tatiana Alejandra-
dc.contributor.other., .-
dc.date.accessioned2022-12-19T21:43:37Z-
dc.date.available2022-12-19T21:43:37Z-
dc.date.issued2018-
dc.identifier.citationUrgiles Sarmiento, T.A. (2018) Incidencia de la adicción de fibras de acero en el hormigón empleado para pavimentos rígidos. Universidad Católica de Cuenca.es_ES
dc.identifier.other10BT2018-TCiv-20-
dc.identifier.urihttps://dspace.ucacue.edu.ec/handle/ucacue/13161-
dc.descriptionEl presente estudio se fundamenta en una comparación de las propiedades mecánicas en estado fresco y endurecido del hormigón simple y el hormigón reforzado con fibra de acero en porcentajes de 0.5%, 1,0% y 1.5%. En el que se realizó el análisis de dos tipos de agregados procedentes de la cantera Santa Isabel y Cochancay para verificar si cumple con los limites de gradación establecidos en la Norma Ecuatoriana NTE INEN 872, para luego fijar un diseño de mezcla patrón empleando el método 211 del ACI para agregados bien gradados y el método gráfico de Fuller y Thompson para agregados que no cumplan las especificaciones granulométricas, utilizando el cemento Guapán Tipo IP y cemento Holcim Tipo GU. Los resultados de los ensayos del comportamiento a compresión se realizó a los 7,14 y 28 días en probetas cilíndricas de 10 cm de diámetro y 20 cm de altura, en donde se estimó que con la adición de 0.5 % de fibra de acero a la mezcla del hormigón se obtuvo un incremento del 17.5% para cementos Guapán Tipo IP y del 28% para cemento Holcim Tipo GU del valor de la resistencia a compresión del hormigón simple . En cuanto a los resultados obtenidos del comportamiento a flexión se ensayó en vigas prismáticas de 15*15*53 cm a los 28 días de curado, en el que en este trabajo de titulación se revela que los especímenes con la adicion del 1% de fibra de acero alcanza una mayor resistencia a flexión del 34% en comparación al hormigón simple para cementos Guapán Tipo IP y para cemento Holcim Tipo GU con 1% de fibra de acero añadida al hormigón logra un 39.6% de la resistencia a flexion para hormigón simple.es_ES
dc.description.abstractThe present study is based on a comparison of the mechanical properties in fresh and hardened state of plain concrete and fiber reinforced concrete steel in percentages of 0.5%, 1.0% and 1.5%. In which the analysis of two types was carried out of aggregates from the Santa Isabel and Cochancay quarries to verify if complies with the gradation limits established in the Ecuadorian Standard NTE INEN 872, to then establish a master mix design using ACI method 211 to well-graded aggregates and the Fuller and Thompson graphical method for aggregates that do not meet the granulometric specifications, using Guapán Type IP cement and Holcim Type GU cement. The results of the compression behavior tests were carried out at 7.14 and 28 days in cylindrical test tubes of 10 cm in diameter and 20 cm in height, where estimated that with the addition of 0.5% of steel fiber to the concrete mix, it was obtained an increase of 17.5% for Guapán Type IP cements and 28% for cement Holcim Type GU of the compressive strength value of simple concrete. In Regarding the results obtained from the flexural behavior, it was tested on beams 15*15*53 cm prismatics after 28 days of curing, in which in this work of titration reveals that the specimens with the addition of 1% steel fiber reach a higher flexural resistance of 34% compared to simple concrete for Guapán Type IP cement and Holcim Type GU cement with 1% steel fiber added to the concrete, it achieves 39.6% of the flexural strength for simple concrete.es_ES
dc.description.sponsorship.es_ES
dc.description.uriTrabajo de investigaciónes_ES
dc.formatapplication/pdfes_ES
dc.format.extentxviii, 85 páginases_ES
dc.language.isospaes_ES
dc.publisherUniversidad Católica de Cuenca.es_ES
dc.relation.es_ES
dc.relation.ispartofseries.;.-
dc.relation.urihttp://creativecommons.org/licenses/by/4.0/deed.eses_ES
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/deed.eses_ES
dc.sourceUniversidad Católica de Cuencaes_ES
dc.sourceRepositorio Institucional - UCACUEes_ES
dc.subjectHormigón simplees_ES
dc.subjecthormigón reforzadoes_ES
dc.subjectfibras de aceroes_ES
dc.subjectensayoses_ES
dc.subjectpropiedade mecánicases_ES
dc.subjectresistenciaes_ES
dc.titleIncidencia de la adicción de fibras de acero en el hormigón empleado para pavimentos rígidoses_ES
dc.title.alternative.es_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
thesis.degree.disciplineIngeniería, Industria y Construcciónes_ES
thesis.degree.grantorUcacue-Sede Azogues. Ingeniería Civiles_ES
thesis.degree.levelTítulo Profesionales_ES
thesis.degree.namePregradoes_ES
thesis.degree.programPresenciales_ES
dc.contributor.cedula0302280409es_ES
dc.identifier.doi.es_ES
dc.coverageAzogues-Ecuadores_ES
dc.subject.ocdeSimple concretees_ES
dc.subject.ocdereinforced concretees_ES
dc.subject.ocdesteel fiberses_ES
dc.subject.ocdetestses_ES
dc.subject.ocdemechanical propertieses_ES
dc.subject.ocderesistances_ES
dc.identifier.journal.es_ES
dc.description.peer-review.es_ES
Aparece en las colecciones: Trabajos de Titulación - Sede Azogues - Ingeniería Civil

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
TESIS INCIDENCIA DE LA ADICION DE FIBRAS DE ACERO EN EL HORMIGÓN EMPLEADO PARA PAVIMENTOS RIGIDOS - TATIANA URGILES.pdfConsultar en biblioteca8.08 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons