Análisis de las propiedades físicos- mecánicas de la mampostería con perforación horizontal sometido a altas temperaturas

Vista sencilla de ítem
dc.contributor.advisorCordero Cabrera, Carlos Julio
dc.contributor.authorAcosta Chilpe, Jefferson Mauricio
dc.contributor.cedula0106700107
dc.contributor.otherGarcía Calle, Anthony Alxander
dc.coverageCuenca - Ecuador
dc.date.accessioned2024-04-04T20:47:36Z
dc.date.available2024-04-04T20:47:36Z
dc.date.issued2024
dc.descriptionEn la actualidad, la mampostería con perforación horizontal es uno de los materiales más utilizados en la construcción debido a su resistencia y durabilidad. Sin embargo, existe falta de conocimiento sobre cómo este material se comporta bajo diferentes condiciones térmicas. Por ende, es crucial analizar las propiedades físicas-mecánicas de la mampostería con perforación horizontal sometido a altas temperaturas en diferentes tiempos de exposición para evaluar el comportamiento estructural. Para iniciar con la investigación se seleccionaron ladrillos de perforación horizontal (tochanos), se elaboraron morteros, viguetas y paneles de ladrillo, con la finalidad de exponerlos a altas temperaturas durante diferentes tiempos (5, 10 y 15 minutos), para ello, se utilizó un soplete, gas doméstico y el horno refractario. Los ensayos de resistencia a compresión reportaron que, el panel de mampostería expuesto a 15 minutos al fuego perdió el 9% de resistencia a la fuerza en comparación con el panel base. El ladrillo expuesto a 15 minutos disminuyó el 37% de resistencia a compresión; en cuanto al mortero expuesto a 15 minutos tuvo una reducción del 58%. El modelo tipo trío perdió un 26% de fuerza de unión tangencial frente al modelo patrón. El ensayo de emisión de gases reportó que el promedio de los niveles de CO en cinco muestras fue de 561 PPM. La trasmisión de calor a mayor temperatura, menor es la diferencia de ºC de la parte indirecta que no estuvo expuesta al fuego. Las viguetas disminuyeron su resistencia a flexión en un 69,5% en relación al modelo patrón.
dc.description.abstractCurrently, horizontal perforated masonry is one of the most widely used materials in construction due to its strength and durability. However, there is a lack of knowledge about how this material behaves under different thermal conditions. Therefore, analyzing the physical-mechanical properties of horizontal perforated masonry subjected to high temperatures at different exposure times is crucial to assessing structural behavior. To start this research, horizontal perforated bricks, and mortars, beams, and brick panels were made to expose them to high temperatures for different times (5, 10, and 15 minutes), using a blowtorch, domestic gas, and a refractory oven. Compression strength tests reported that the masonry panel exposed to 15 minutes of fire lost 9% of strength compared to the base panel. The brick exposed for 15 minutes decreased by 37% in compression strength. The mortar exposed for 15 minutes showed a 58% reduction. The trio model lost 26% of tangential bond strength compared to the standard model. The gas emission test indicated that the average CO levels in five samples were 561 PPM. Heat transmission at higher temperatures resulted in a minor temperature difference in the indirect part not exposed to fire. Beams decreased their flexural strength by 69.5% compared to the standard model.
dc.description.uriTesis
dc.formatapplication/pdf
dc.format.extent99 páginas
dc.identifier.citationAPA
dc.identifier.other5BT2024-TC14
dc.identifier.urihttps://dspace.ucacue.edu.ec/handle/ucacue/17114
dc.language.isospa
dc.publisherUniversidad Católica de Cuenca.es_ES
dc.relationProyecto de Titulación
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rightsAtribución 4.0 Internacionales_ES
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/deed.eses_ES
dc.sourceUniversidad Católica de Cuencaes_ES
dc.sourceRepositorio Institucional - UCACUEes_ES
dc.subjectMAMPOSTERÍA HORIZONTAL
dc.subjectPANELES
dc.subjectPROPIEDADES FÍSICAS Y MECÁNICAS
dc.subjectFUEGO CONTROLADO
dc.subjectALTAS TEMPERATURAS
dc.titleAnálisis de las propiedades físicos- mecánicas de la mampostería con perforación horizontal sometido a altas temperaturas
dc.typeinfo:eu-repo/semantics/bachelorThesis
thesis.degree.disciplineIngeniería Civil
thesis.degree.grantorUniversidad Católica de Cuenca. Unidad Académica de Ingeniería, Industria y Construcción. Carrera de Ingeniería Civil
thesis.degree.levelTítulo Profesional
thesis.degree.nameIngeniero Civil
thesis.degree.programPresencial
Archivos
Bloque original
Mostrando 1 - 1 de 1
Miniatura
Nombre:
ACOSTA CHILPE JEFFERSON MAURICIO.pdf
Tamaño:
4.85 MB
Formato:
Adobe Portable Document Format
Descripción:
Descargar
Bloque de licencias
Mostrando 1 - 1 de 1
Miniatura
Nombre:
license.txt
Tamaño:
1.27 KB
Formato:
Item-specific license agreed upon to submission
Descripción:
Descargar
Colecciones
Trabajos de Titulación - Ingeniería Civil